В Пластиковый прототип производство промышленность, Пса (Полистирол) blow molding prototype parts are widely used in industries such as packaging, Электроника, и игрушки. This is due to PS’s excellent transparency, бюджетный, and easy processing. Однако, processing PS blow molding prototypes is not without difficulties. Many manufacturers encounter problems like poor thermal stability during molding, brittle prototype parts, and uneven wall thickness. This article will break down the entire processing process of PS blow molding prototype parts based on four core themes, providing targeted solutions to common issues and helping you produce high-quality PS prototypes efficiently.
1. PS Material Properties: Understand the “Character” of the Material First
Before starting the processing of PS blow molding prototype parts, it is essential to have a deep understanding of PS material properties. Unlike PP or PVC, PS has unique characteristics that directly affect every link of the blow molding process. Mastering these properties can help avoid many common processing mistakes.
1.1 Key Properties of PS and Their Impact on Processing
| Свойство | Specifics | Impact on Blow Molding Prototype Processing |
| Плотность | 1.04-1.06 G/CM³ (higher than PP, lower than PVC) | Higher density means PS prototypes are slightly heavier than PP ones; it also affects material flow rate during extrusion—slower than PP, requiring precise control of extrusion speed. |
| Тепловая стабильность | Точка плавления (150-160℃), thermal decomposition temperature (＞250℃); easy to soften at high temperatures and brittle at low temperatures | During blow molding, the temperature range for PS is narrow (150-180℃). Exceeding 180℃ causes yellowing; below 140℃ leads to poor material fluidity and difficulty in forming. |
| Механическая прочность | Предел прочности (40-60 МПА), воздействие сила (1.5-3 KJ /); хрупкий, easy to break when impacted | PS prototypes are not suitable for load-bearing or impact-resistant scenarios (НАПРИМЕР., Автомобильные внешние детали). Need to avoid sharp corners in design to reduce stress concentration and prevent cracking. |
| Химическая устойчивость | Resistant to dilute acids, щелочи, and alcohols; easily corroded by oils, ketones, and aromatic hydrocarbons | When choosing coolants or cleaning agents during processing, avoid oil-based products. For prototypes used to hold chemicals, ensure the contained substances do not react with PS. |
Общий вопрос здесь: Why are PS blow molding prototypes often brittle? The main reason lies in PS’s inherent molecular structure—it has low impact strength. To improve this, you can add 5-10% rubber modifiers (НАПРИМЕР., styrene-butadiene rubber) to the PS material, which can increase the impact strength to 5-8 kJ/m² and make the prototype less brittle. Однако, note that adding modifiers will slightly reduce PS’s transparency.
2. Blow Molding Technology: Choose the Right “Инструмент” for the Job
Blow molding technology is the core of PS blow molding prototype parts processing. Для PS, which has poor thermal stability and brittle properties, choosing the appropriate blow molding method and optimizing key parameters is crucial to ensuring prototype quality.
2.1 Comparison of Two Common Blow Molding Technologies for PS
| Технология | Принцип работы | Advantages for PS Prototypes | Disadvantages for PS Prototypes | Suitable PS Prototype Types |
| Extrusion Blow Molding | Melt PS into a tube-shaped parison via an extruder, then clamp it in a mold, inject air to inflate it, and cool to form | Simple process, low equipment investment; suitable for small-batch PS prototypes; easy to adjust parison thickness for uneven-walled prototypes. | Poor parison stability (PS’s high viscosity leads to easy parison sagging); low precision, difficult to control tolerances within ±0.1mm. | Large PS prototypes (НАПРИМЕР., toy shells, large packaging boxes) with low precision requirements. |
| Injection Blow Molding | First inject PS into a preform mold to make a preform, then transfer the preform to a blow mold, inject air to inflate, and cool to form | Высокая точность (tolerances up to ±0.05mm); uniform wall thickness; smooth prototype surface, Хорошая прозрачность (ideal for PS’s transparent advantage). | Complex equipment, high investment cost; not suitable for large PS prototypes (preform size is limited). | Маленький, high-precision PS prototypes (НАПРИМЕР., cosmetic bottle caps, корпуса электронных компонентов) with high transparency requirements. |
2.2 Key Parameters in PS Blow Molding Process
No matter which blow molding technology is chosen, the following key parameters must be strictly controlled for PS prototypes:
- Parison Formation: For extrusion blow molding, the extruder temperature should be set in sections: feed zone (140-150℃), melting zone (150-160℃), die head (160-170℃). The parison extrusion speed should be 8-15mm/s (slower than PP) to prevent parison sagging. For injection blow molding, the preform injection temperature is 155-165℃, and the injection pressure is 60-80MPa to ensure the preform is dense.
- Blow Ratio: The blow ratio for PS is 1.5-2.5:1 (lower than PP’s 2-4:1). Exceeding 2.5:1 will cause the PS prototype wall to be too thin and brittle; меньше, чем 1.5:1 leads to material waste and uneven cooling.
- Дизайн плесени: The mold cavity surface should be highly polished (Ra 0.4-0.8μm) to maintain PS’s transparency. The draft angle should be 2-3° (larger than PP’s 1-3°) because PS has high friction and is easy to stick to the mold. For injection blow molding, the preform mold should have a smooth inner wall to avoid affecting the preform’s surface quality.
3. Prototype Parts Design: Lay the Foundation for Smooth Processing
Prototype parts design directly affects whether the PS blow molding process can proceed smoothly and whether the final prototype meets the requirements. 不合理的设计 often leads to processing defects such as cracking, деформация, and uneven wall thickness.
3.1 Core Design Principles for PS Blow Molding Prototypes
| Дизайн элемент | Requirements for PS Prototypes | Обоснование | Практический пример |
| Моделирование CAD | Используйте программное обеспечение, такое как SolidWorks, Autocad; ensure 3D model accuracy (tolerance ±0.05mm for key dimensions) | Accurate modeling provides a reliable basis for mold making and parameter setting. For PS prototypes with high transparency requirements, the model should avoid complex structures that affect light transmission. | When designing a PS cosmetic bottle prototype, the CAD model should clearly mark the bottle mouth diameter (20мм), высота (100мм), and wall thickness (1.0± 0,1 мм). |
| Part Geometry | Избегайте острых углов (radius ≥3mm); minimize complex structures like undercuts and deep grooves | Sharp corners cause stress concentration (PS is brittle, easy to crack here); undercuts and deep grooves make demolding difficult and increase the risk of prototype damage. | For a PS toy car body prototype, design the corners of the car roof as arcs (R=5mm) instead of right angles; integrate small protruding structures into the main body to avoid undercuts. |
| Толщина стены | Равномерная толщина (variation ≤5%); minimum thickness ≥0.8mm (Для небольших прототипов), ≥1.2mm (for large prototypes) | PS has poor impact strength; too thin walls (＜0.8mm) lead to brittle prototypes; uneven thickness causes uneven cooling and deformation. | For a PS storage box prototype (200×150×100mm), design the wall thickness as 1.2±0.05mm; the bottom thickness can be increased to 1.5mm to enhance stability, but the transition should be smooth. |
| Допуски | For extrusion blow molding: ±0.1-0.2mm; for injection blow molding: ±0.05-0.1mm; avoid overly tight tolerances (＜0.05mm) | PS has poor dimensional stability after molding; overly tight tolerances are difficult to achieve and increase production costs. | For a PS electronic component casing prototype, the key mounting hole diameter tolerance can be set to ±0.1mm (injection blow molding) to ensure assembly accuracy without increasing processing difficulty. |
| Дизайн для производства | Simplify the structure as much as possible; reserve trimming allowance (0.5-1мм) at the mold parting line | Reduces processing difficulty and defect rates; trimming allowance ensures that excess material at the parting line can be removed without damaging the prototype. | For a PS bottle prototype with a handle, design the handle as a separate part (to be assembled after blow molding) instead of an integrated structure, which simplifies the mold design and blow molding process. |
4. Методы обработки: Master the “Skills” to Improve Quality
Processing techniques are the key to turning PS raw materials into high-quality blow molding prototypes. For PS’s characteristics of poor thermal stability and brittleness, targeted processing techniques must be adopted to solve common problems.
4.1 Key Processing Techniques for PS Blow Molding Prototypes
| Technique Category | Specific Methods | Сценарии приложения & Solutions to Common Problems |
| Heating Methods | Extruder section heating (for extrusion blow molding); preform heating (for injection blow molding: infrared heating, temperature 160-170℃) | Проблема: PS yellowing during heating. Решение: Strictly control the heating temperature (not exceeding 170℃); shorten the material residence time in the extruder (screw speed 30-50rpm). |
| Cooling Systems | Water cooling (mold cooling: water temperature 15-25℃); Воздушное охлаждение (prototype post-cooling: wind speed 1-2m/s) | Проблема: PS prototype deformation after demolding. Решение: Extend the mold cooling time (8-12 seconds for small prototypes, 15-20 seconds for large ones); after demolding, Поместите прототип на охлаждающую стойку для 10-15 минуты (room temperature 20-25℃) to stabilize dimensions. |
| Material Flow Control | Use a screw with a shallow groove (depth 3-5mm) for extrusion; добавлять 0.5-1% lubricant (НАПРИМЕР., stearic acid) to PS raw materials | Проблема: Poor PS material flow, uneven parison. Решение: The shallow-groove screw enhances shearing and mixing of PS; lubricants improve flowability without affecting transparency. |
| Выбор инструментов | Extrusion blow molding: die head with smooth inner wall (RA 0,4 мкм); injection blow molding: preform mold with chrome plating (Улучшает устойчивость к износу) | Проблема: PS parison has scratches or uneven thickness. Решение: Regularly polish the die head inner wall to remove impurities; check the preform mold for wear and replace it in time (chrome-plated molds have a service life 2-3 times longer than ordinary steel molds). |
| Оптимизация процесса | Усыновить “низкая температура, slow speed” for extrusion blow molding (temperature 150-170℃, speed 8-12mm/s); for injection blow molding, optimize preform cooling time (5-8 секунды) | Проблема: High defect rate of PS prototypes (трещины, пожелтение). Решение: Low temperature and slow speed reduce PS thermal decomposition and parison sagging; reasonable preform cooling time ensures the preform maintains its shape during transfer to the blow mold. |
5. Yigu Technology’s Perspective on PS Blow Molding Prototype Processing
В Yigu Technology, мы фокусируемся на “material-technology-design integration” for PS blow molding prototypes. We select high-transparency GPPS (General Purpose Polystyrene) for most prototypes, добавление 3-5% rubber modifiers for brittle-sensitive scenarios. For blow molding, we prefer injection blow molding for small, Высокие детали (tolerances ±0.05mm) and optimize heating with infrared temperature control (accuracy ±2℃). In design, we use CAD modeling with DFM to avoid sharp corners (R≥3mm) and control wall thickness variation ≤5%. Quality control includes 100% Визуальный осмотр (прозрачность, трещины) и 15% sampling for impact strength tests. The core is leveraging PS’s advantages while mitigating its brittleness and thermal stability issues to deliver cost-effective, Высококачественные прототипы.
Часто задаваемые вопросы
1. Why does my PS blow molding prototype turn yellow during processing?
Yellowing is mainly caused by excessive heating temperature or prolonged material residence time. Первый, check the extruder/mold temperature—reduce the die head temperature by 5-10℃ (to 160-165℃) and the melting zone temperature by 10-15℃ (to 145-155℃). Второй, increase the screw speed by 5-10rpm (to 35-40rpm) to shorten the material residence time in the extruder. If yellowing persists, replace the PS raw material (it may have been stored for too long and degraded).
2. How to improve the impact resistance of PS blow molding prototypes without significantly reducing transparency?
The best way is to use impact-modified PS (БЕДРА, Высокий удар полистирол) instead of ordinary GPPS. HIPS adds rubber particles during production, which can increase impact strength to 5-10 KJ / (3-5 times that of GPPS) во время поддержания 80-90% of GPPS’s transparency. If you must use GPPS, добавлять 3-5% transparent rubber modifiers (НАПРИМЕР., methyl methacrylate-butadiene-styrene copolymer, MBS), which can increase impact strength by 2-3 times with only a 5-10% reduction in transparency.
3. What is the best way to solve the problem of PS blow molding prototype sticking to the mold?
Первый, optimize the mold design: increase the draft angle to 2.5-3° (larger than the usual 2°) and polish the mold cavity surface to Ra 0.4μm (higher than the usual 0.8μm). Второй, use a mold release agent suitable for PS—choose water-based mold release agents (avoid oil-based ones, which affect PS’s transparency) and spray a thin layer (0.01-0.02мм) on the mold cavity before each molding cycle. Третий, extend the mold cooling time by 2-3 секунды (к 10-13 seconds for small prototypes) to make the PS prototype harder when demolding and less likely to stick to the mold.