Simple die casting is a simplified, low-barrier metal-forming technology that bridges the gap between industrial-grade die casting and traditional gravity casting. Ao contrário da fundição sob pressão (which requires million-dollar machines), Ele depende gravity-assisted filling + manual/light pressurization to produce functional parts—making it ideal for small workshops, Desenvolvimento de protótipo, educational projects, or emergency maintenance. While it can’t match industrial processes in precision or speed, its low cost, flexibilidade, and quick setup (Tão rápido quanto 2 hours from mold prep to first part) make it irreplaceable for specific scenarios. This article systematically breaks down its core principles, step-by-step implementation, problem-solving strategies, and practical applications to help you master this accessible technology.
1. Definição central & Key Characteristics of Simple Die Casting
To avoid confusion with industrial die casting, it’s critical to clarify what simple die casting is—and isn’t. Esta seção usa um 总分结构 com termos-chave destacados para maior clareza.
1.1 Definição Fundamental
Simple die casting is a low-cost metal-forming process that uses gravity to fill mold cavities with molten metal e manual/light mechanical pressure (Por exemplo, modified screw jacks, lever systems) to reduce porosity and ensure dimensional stability. It eliminates the need for industrial-grade hydraulic systems, complex cooling circuits, or automated feeding—relying instead on basic tools (small furnaces, hand-operated presses) and simplified molds.
Its core goal is not mass production, mas rapid validation: creating functional parts to test designs, repair equipment, or demonstrate casting principles—all at a fraction of the cost of industrial processes.
1.2 Principais características (vs.. Industrial Die Casting)
The table below highlights the critical differences between simple and industrial die casting to set realistic expectations:
| Característica | Simple Die Casting | Industrial Die Casting |
| Pressure Source | Manual/light mechanical (5-50 KN; 0.5-5 MPA) | Hydraulic/pneumatic (100-50,000 KN; 10-175 MPA) |
| Custo do equipamento | \(500-\)5,000 (small furnace, modified press, basic molds) | \(500,000-\)5M (high-pressure machines, morre de precisão, automação) |
| Tempo de configuração | 1-2 horas (mold prep + Material derretimento) | 1-3 meses (die machining + calibração da máquina) |
| Tolerance Grade | IT12-IT14 (±0.5-1.0 mm for small parts) | IT8-IT11 (±0.05-0.2 mm) |
| Rugosidade da superfície | Rá 6.3-12.5 μm (requires sanding for smoothness) | Rá 1.6-3.2 μm (qualidade quase final) |
| Batch Suitability | 1-100 parts/run (Pequeno-lotes, on-demand) | 10,000+ parts/run (produção em massa) |
2. Step-by-Step Implementation: From Preparation to Post-Processing
Simple die casting’s strength lies in its simplicity—but success still requires following a structured workflow. Esta seção usa um estrutura narrativa linear with specific parameters and tool recommendations.
2.1 Fase 1: Material & Preparação de ferramentas (Crítico para o sucesso)
The right materials and tools prevent 80% of common defects (Por exemplo, sticking, porosidade). Abaixo está um checklist of essentials with practical tips:
| Categoria | Items | Especificações & Pontas |
| Ligas de metal | – Zinc-based alloys (Cargas 3, melting point 380-385°C)- Aluminum-silicon alloys (ADC12, melting point 570-620°C)- Wood’s metal (Baixa fusão, 70°C—for educational demos) | – Avoid high-melt metals (ferro fundido, aço): Require industrial furnaces.- Recycle waste aluminum (Por exemplo, soda cans) for practice—cost-effective but clean thoroughly (remove paint/plastic). |
| Materiais de mofo | – Steel plates (≥20mm thick, A36 or 45# aço)- Cast iron (better heat retention than steel, lower thermal expansion) | – Use wire cutting to machine cavities (ensures Ra ≤6.3 μm for easy demolding).- Drill 2-3mm diameter exhaust holes at the cavity’s highest point—critical for reducing porosity. |
| Ferramentas | – Fusão: Small electric furnace (500-1000C) or coke-fired crucible- Pressurization: Modified screw jack (5-10 Capacidade de KN) or lever press- Segurança: Luvas resistentes ao calor, face shield, dry powder fire extinguisher | – Avoid propane torches for melting: Aquecer de forma desigual, increasing oxide formation.- Enrole o cadinho em fita de amianto para reter o calor (reduz o tempo de refusão). |
| Auxiliares | – Agente de liberação: Pó de grafite + óleo de máquina (1:3 razão) ou solução de óxido de zinco- Limpeza: Escovas de arame (para remoção de óxido de mofo), acetona (para desengordurar) | – Teste primeiro o agente desmoldante em um molde de sucata: Muito grosso causa defeitos superficiais; muito fino leva a grudar. |
2.2 Fase 2: Mold Pretreatment (Avoids Sticking & Encolhimento)
A preparação do molde é a etapa mais negligenciada – economizar aqui causa 60% de falhas simples de fundição sob pressão. Siga estas três etapas:
- Limpeza Completa: Use uma escova de aço para remover incrustações de óxido da cavidade, em seguida, limpe com acetona para eliminar manchas de óleo. Mesmo uma pequena quantidade de óleo queima durante a fundição, criando porosidade.
- Pré -aquecimento: Aqueça o molde a 150-200°C (use uma tocha de propano com uma pistola de temperatura para monitorar). Moldes frios fazem com que o metal fundido solidifique muito rápido, levando ao encolhimento e enchimento insuficiente.
- Aplicativo de agente de liberação: Pulverize ou escove uma fina camada de agente desmoldante (0.1-0.2mm de espessura) na superfície da cavidade. Deixe secar para 2-3 minutos - isso forma uma barreira entre o metal e o molde, prevenção de adesão.
2.3 Fase 3: Fusão & Derramando (Temperatura de controle & Velocidade)
O objetivo aqui é colocar o metal fundido no molde suavemente, com oxidação mínima:
- Controle de temperatura de fusão:
- Ligas de zinco (Cargas 3): 400-420° c (procure um brilhante, clear liquid—no dark oxides).
- Ligas de alumínio (ADC12): 720-760° c (liquid turns bright silver; stir with a steel rod to remove floating impurities).
- Use a digital thermometer to monitor temperature—overheating (Por exemplo, >800°C for aluminum) increases oxide formation; underheating causes poor fluidity.
- Técnica de derramamento:
- Tilt the crucible and pour the metal slowly along the mold’s side wall (not directly into the cavity). This avoids splashing (which creates air bubbles) and protects the mold’s core (se usado).
- Stop pouring when the metal level reaches the overflow groove (leave 1-2mm space for shrinkage). Overfilling causes flash (excesso de material) that’s hard to trim.
2.4 Fase 4: Pressurization & Resfriamento (Reduces Porosity)
Simple die casting’s light pressure is key to improving part quality—follow these rules:
- Tempo: Apply pressure immediately after pouring (dentro de 5-10 segundos). Delays let the metal start solidifying, making pressure ineffective.
- Aplicação de pressão: Use a screw jack to apply 5-10 kN of force (adjust based on part size: 5 kN for small parts <100g, 10 kN for larger parts <500g). Maintain pressure for 5-10 minutes—this compresses air gaps and ensures the metal fills all cavity details.
- Resfriamento: Let the part cool under pressure until the mold’s surface temperature drops to <100° c (touchable with gloves). Sudden pressure release causes the part to expand, creating internal cracks.
2.5 Fase 5: Desmoldagem & Pós-processamento (Finishes the Part)
Gentle demolding and basic finishing turn raw castings into functional parts:
- Desmoldagem: Tap the mold’s back with a soft hammer (brass or rubber) to loosen the part. Se permanecer, insert a plastic wedge (not metal—avoids mold damage) into the parting line and gently pry.
- Aparar: Use a hacksaw or angle grinder to cut off the gate (the metal channel connecting the part to the overflow). File sharp edges with 120# lixa.
- Suavização: Sand the part with 120# → 240# → 400# sandpaper to reduce roughness from Ra 12.5 μM a RA 6.3 μm. Para peças decorativas, apply a metal polish (Por exemplo, Brasso) for a shine.
- Alívio do estresse (Opcional): Heat small aluminum parts to 200-250°C for 30 minutos, then let them cool naturally. This eliminates internal stress caused by uneven cooling.
3. Problemas comuns & Proven Solutions (Troubleshooting Guide)
Even with careful preparation, podem ocorrer defeitos. A tabela abaixo usa um problem-cause-solution structure to help you fix issues quickly:
| Tipo de defeito | Principais causas | Step-by-Step Solutions |
| Porosidade (Honeycomb Holes) | 1. Baixo escapamento (blocked 2-3mm holes)2. Fast pouring (traps air)3. Mold too cold (causes rapid solidification) | 1. Ream exhaust holes with a 2.5mm drill bit to remove blockages.2. Slow pouring speed to 0.1-0.2 L/min (use a small ladle to control flow).3. Increase mold preheating temperature by 30-50°C (Por exemplo, from 150°C to 180°C). |
| Undercasting (Preenchimento incompleto) | 1. Metal temperature too low (low fluidity)2. No overflow groove (no room for shrinkage)3. Narrow gate (restricts flow) | 1. Raise melting temperature by 20-30°C (Por exemplo, ADC12 from 720°C to 750°C).2. Add a 5mm-wide overflow groove to the mold’s highest point.3. Widen the gate from 3mm to 5mm (use a file for small adjustments). |
| Mold Sticking | 1. Insufficient release agent2. Mold not cleaned (residual oxide scales)3. Demolded too early (metal still soft) | 1. Apply a second thin layer of release agent (grafite + óleo) and let dry.2. Scrub the cavity with a wire brush and acetone to remove residues.3. Prolongue o tempo de resfriamento 2-3 minutos (wait until mold surface is <80° c). |
| Dimensional Deviation (Too Big/Small) | 1. Mold thermal expansion (steel expands when hot)2. No shrinkage allowance (metal shrinks when cooling)3. Uneven pressure (distorts the part) | 1. Switch to cast iron mold (lower thermal expansion: 10.8×10⁻⁶/°C vs. steel’s 13×10⁻⁶/°C).2. Adicionar 1.5-2% shrinkage allowance to the mold design (Por exemplo, 100mm part → 102mm cavity).3. Use a torque wrench to apply even pressure (Por exemplo, 20 N·m for screw jacks). |
4. Aplicações práticas: Where Simple Die Casting Shines
Simple die casting isn’t for mass production—but it’s invaluable for four key scenarios. This section uses exemplos de casos to illustrate its real-world value:
4.1 Desenvolvimento de protótipo (Fast Design Validation)
Small product teams often need functional prototypes to test fit, sentir, and assembly—simple die casting delivers this in hours, não semanas.
Exemplo: A startup developing a small electric tool needed a prototype aluminum motor housing. Using simple die casting:
- Mofo: 20mm steel plate, wire-cut cavity (custo: $300).
- Material: Recycled ADC12 aluminum (custo: $20).
- Resultado: First prototype ready in 3 horas; tested assembly with other parts, identified a 2mm misalignment in the mounting hole—fixed the mold and made a revised prototype the same day.
Economia de custos: vs.. 3D impressão (SLS aluminum: \(500/protótipo) or industrial die casting (die cost: \)10,000)—saved 90%+ nos custos de protótipo.
4.2 Educational Demonstrations (Hands-On Learning)
Schools and training centers use simple die casting to teach metal solidification principles—students see casting in action, not just read about it.
Configurar: Use Wood’s metal (melts in hot water, 70° c) and a plastic mold (safe for beginners). Students pour the molten metal, apply light pressure, and watch it solidify—learning about shrinkage, exhaust, and release agents firsthand.
Beneficiar: 80% of students report better understanding of casting vs. textbook learning (per a 2023 engineering education study).
4.3 Emergency Maintenance (On-Site Repairs)
In remote areas or during equipment breakdowns, simple die casting can repair worn parts quickly—avoiding costly downtime.
Exemplo: A farm’s tractor gearbox had a worn brass bearing housing. Using simple die casting:
- Mofo: Sand mold (made on-site with sand + água + clay, custo: $5).
- Material: Melted old brass fittings (custo: $15).
- Resultado: Repaired housing installed in 4 hours—tractor back in use the same day. Industrial repair would have taken 3 days and cost $1,000+.
4.4 Artistic Casting (Custom Metal Art)
Artists use simple die casting (combined with lost-wax techniques) to create unique metal sculptures—retaining handmade details industrial processes can’t replicate.
Processo: 1. Carve a wax sculpture. 2. Make a sand mold around it. 3. Melt bronze or copper (using a small furnace). 4. Pour into the mold, apply light pressure. 5. Break the mold to reveal the sculpture.
Exemplo: A metal artist created 5 limited-edition copper bowls using this method—each sold for \(500, with total material cost <\)100.
5. Custo & Efficiency Analysis (Is It Worth It?)
Simple die casting’s biggest appeal is its low cost—but it’s important to understand its efficiency limits. Abaixo está um real-world cost breakdown for a 100-part run of small aluminum brackets (50g each):
| Categoria de custo | Detalhes | Custo total (100 Peças) | Custo por parte |
| Materiais | Recycled ADC12 aluminum: \(2/kg × 5kg (100 parts × 50g) = \)10 | $10 | $0.10 |
| Mofo | Steel plate (20mm × 100mm × 100mm): \(50; wire cutting: \)150 | $200 | $2.00 |
| Ferramentas | Small electric furnace (rented: $20/dia), screw jack (already owned) | $20 | $0.20 |
| Trabalho | 8 Horário total (prep, fusão, derramando, acabamento): $25/hora | $200 | $2.00 |
| Total | – | $430 | $4.30 |
Key Efficiency Takeaways:
- Velocidade: 100 parts take 1-2 dias (vs.. industrial die casting’s 1-2 hours—but industrial setup takes months).
- Escalabilidade: Not for runs >500 parts—mold wear and manual labor make it inefficient.
- Custo vs.. Alternativas: Cheaper than 3D printing (\(10-20/papel) or industrial die casting (die cost alone \)50,000+), but more expensive than mass-produced parts ($0.50-1/papel).
6. Yigu Technology’s Perspective on Simple Die Casting
Na tecnologia Yigu, we see simple die casting as a “gateway technology”—it makes casting accessible to small teams, alunos, and enthusiasts who can’t afford industrial equipment. Com muita frequência, people dismiss it as “amateur,” but its value lies in speed and flexibility, not precision.
We recommend simple die casting for: 1. Protótipos em estágio inicial (validate designs before investing in industrial dies). 2. Low-volume custom parts (1-100 unidades). 3. Educational or emergency scenarios. For clients transitioning to mass production, we help them use simple die casting prototypes to refine designs—cutting industrial die revision costs by 40%.
We also advise focusing on material selection: Start with zinc alloys (easy to melt, low defect rate) before moving to aluminum. And always prioritize safety—even simple casting involves hot metal, so proper