Dans le fabrication de prototypes en plastique industrie, Ps (Polystyrène) Pièces prototypes de moulage par soufflage sont largement utilisés dans des industries telles que l'emballage, électronique, et des jouets. This is due to PS’s excellent transparency, faible coût, and easy processing. Cependant, processing PS blow molding prototypes is not without difficulties. Many manufacturers encounter problems like poor thermal stability during molding, brittle prototype parts, and uneven wall thickness. This article will break down the entire processing process of PS blow molding prototype parts based on four core themes, providing targeted solutions to common issues and helping you produce high-quality PS prototypes efficiently.
1. PS Material Properties: Understand the “Character” of the Material First
Before starting the processing of PS blow molding prototype parts, it is essential to have a deep understanding of PS material properties. Unlike PP or PVC, PS has unique characteristics that directly affect every link of the blow molding process. Mastering these properties can help avoid many common processing mistakes.
1.1 Key Properties of PS and Their Impact on Processing
| Propriété | Détails | Impact sur le traitement du prototype de moulage par soufflage |
| Densité | 1.04-1.06 g / cm³ (higher than PP, lower than PVC) | Higher density means PS prototypes are slightly heavier than PP ones; it also affects material flow rate during extrusion—slower than PP, requiring precise control of extrusion speed. |
| Stabilité thermique | Point de fusion (150-160℃), Température de décomposition thermique (＞250℃); easy to soften at high temperatures and brittle at low temperatures | During blow molding, the temperature range for PS is narrow (150-180℃). Exceeding 180℃ causes yellowing; below 140℃ leads to poor material fluidity and difficulty in forming. |
| Résistance mécanique | Résistance à la traction (40-60 MPA), force d'impact (1.5-3 KJ /); fragile, easy to break when impacted | PS prototypes are not suitable for load-bearing or impact-resistant scenarios (Par exemple, pièces extérieures automobiles). Need to avoid sharp corners in design to reduce stress concentration and prevent cracking. |
| Résistance chimique | Resistant to dilute acids, alcalis, and alcohols; easily corroded by oils, ketones, and aromatic hydrocarbons | When choosing coolants or cleaning agents during processing, avoid oil-based products. For prototypes used to hold chemicals, ensure the contained substances do not react with PS. |
Une question courante ici est: Why are PS blow molding prototypes often brittle? The main reason lies in PS’s inherent molecular structure—it has low impact strength. To improve this, you can add 5-10% rubber modifiers (Par exemple, styrene-butadiene rubber) to the PS material, which can increase the impact strength to 5-8 kJ/m² and make the prototype less brittle. Cependant, note that adding modifiers will slightly reduce PS’s transparency.
2. Technologie de moulage par soufflage: Choisissez le bon “Outil” for the Job
Technologie de moulage par soufflage is the core of PS blow molding prototype parts processing. Pour ps, which has poor thermal stability and brittle properties, choosing the appropriate blow molding method and optimizing key parameters is crucial to ensuring prototype quality.
2.1 Comparison of Two Common Blow Molding Technologies for PS
| Technologie | Principe de travail | Advantages for PS Prototypes | Disadvantages for PS Prototypes | Suitable PS Prototype Types |
| Moulage de coup d'extrusion | Melt PS into a tube-shaped parison via an extruder, then clamp it in a mold, inject air to inflate it, and cool to form | Processus simple, Faible investissement d'équipement; suitable for small-batch PS prototypes; easy to adjust parison thickness for uneven-walled prototypes. | Mauvaise stabilité de la parhamètre (PS’s high viscosity leads to easy parison sagging); faible précision, difficult to control tolerances within ±0.1mm. | Large PS prototypes (Par exemple, coquilles de jouets, large packaging boxes) with low precision requirements. |
| Moulage par coup d'injection | First inject PS into a preform mold to make a preform, puis transférez la préforme dans un moule à souffler, injecter de l'air pour gonfler, and cool to form | Haute précision (tolerances up to ±0.05mm); épaisseur de paroi uniforme; smooth prototype surface, bonne transparence (ideal for PS’s transparent advantage). | Équipement complexe, Coût d'investissement élevé; not suitable for large PS prototypes (preform size is limited). | Petit, high-precision PS prototypes (Par exemple, cosmetic bottle caps, boîtiers de composants électroniques) with high transparency requirements. |
2.2 Key Parameters in PS Blow Molding Process
No matter which blow molding technology is chosen, the following key parameters must be strictly controlled for PS prototypes:
- Formation de paraison: Pour la moulure de soufflage d'extrusion, the extruder temperature should be set in sections: zone d'alimentation (140-150℃), zone de fusion (150-160℃), tête de décès (160-170℃). The parison extrusion speed should be 8-15mm/s (plus lent que PP) to prevent parison sagging. Pour le moulage par coup d'injection, the preform injection temperature is 155-165℃, and the injection pressure is 60-80MPa to ensure the preform is dense.
- Rapport de soufflage: The blow ratio for PS is 1.5-2.5:1 (plus bas que les PP 2-4:1). Exceeding 2.5:1 will cause the PS prototype wall to be too thin and brittle; moins que 1.5:1 leads to material waste and uneven cooling.
- Conception de moisissure: The mold cavity surface should be highly polished (Ra 0.4-0.8μm) to maintain PS’s transparency. The draft angle should be 2-3° (larger than PP’s 1-3°) because PS has high friction and is easy to stick to the mold. Pour le moulage par coup d'injection, the preform mold should have a smooth inner wall to avoid affecting the preform’s surface quality.
3. Prototype Parts Design: Lay the Foundation for Smooth Processing
Prototype parts design directly affects whether the PS blow molding process can proceed smoothly and whether the final prototype meets the requirements. 不合理的设计 often leads to processing defects such as cracking, déformation, and uneven wall thickness.
3.1 Core Design Principles for PS Blow Molding Prototypes
| Élément de conception | Requirements for PS Prototypes | Raisonnement | Exemple pratique |
| Modélisation CAO | Utiliser un logiciel comme SolidWorks, Autocad; ensure 3D model accuracy (tolerance ±0.05mm for key dimensions) | Accurate modeling provides a reliable basis for mold making and parameter setting. For PS prototypes with high transparency requirements, the model should avoid complex structures that affect light transmission. | When designing a PS cosmetic bottle prototype, the CAD model should clearly mark the bottle mouth diameter (20MM), hauteur (100MM), and wall thickness (1.0± 0,1 mm). |
| Géométrie en partie | Évitez les coins pointus (rayon ≥3mm); minimize complex structures like undercuts and deep grooves | Sharp corners cause stress concentration (PS is brittle, easy to crack here); undercuts and deep grooves make demolding difficult and increase the risk of prototype damage. | For a PS toy car body prototype, design the corners of the car roof as arcs (R=5mm) instead of right angles; integrate small protruding structures into the main body to avoid undercuts. |
| Épaisseur de paroi | Épaisseur uniforme (variation ≤5%); minimum thickness ≥0.8mm (pour les petits prototypes), ≥1.2mm (pour les grands prototypes) | PS has poor impact strength; too thin walls (＜0.8mm) lead to brittle prototypes; uneven thickness causes uneven cooling and deformation. | For a PS storage box prototype (200×150×100mm), design the wall thickness as 1.2±0.05mm; the bottom thickness can be increased to 1.5mm to enhance stability, but the transition should be smooth. |
| Tolérances | Pour la moulure de soufflage d'extrusion: ±0,1-0,2 mm; pour le moulage par coup d'injection: ±0,05-0,1 mm; avoid overly tight tolerances (＜ 0,05 mm) | PS has poor dimensional stability after molding; overly tight tolerances are difficult to achieve and increase production costs. | For a PS electronic component casing prototype, the key mounting hole diameter tolerance can be set to ±0.1mm (moulage par coup d'injection) to ensure assembly accuracy without increasing processing difficulty. |
| Conception pour la fabrication | Simplify the structure as much as possible; reserve trimming allowance (0.5-1MM) at the mold parting line | Reduces processing difficulty and defect rates; trimming allowance ensures that excess material at the parting line can be removed without damaging the prototype. | For a PS bottle prototype with a handle, design the handle as a separate part (to be assembled after blow molding) instead of an integrated structure, which simplifies the mold design and blow molding process. |
4. Techniques de traitement: Maître le “Skills” to Improve Quality
Techniques de traitement are the key to turning PS raw materials into high-quality blow molding prototypes. For PS’s characteristics of poor thermal stability and brittleness, targeted processing techniques must be adopted to solve common problems.
4.1 Key Processing Techniques for PS Blow Molding Prototypes
| Catégorie de technique | Méthodes spécifiques | Scénarios d'application & Solutions to Common Problems |
| Heating Methods | Extruder section heating (for extrusion blow molding); preform heating (pour le moulage par coup d'injection: infrared heating, temperature 160-170℃) | Problème: PS yellowing during heating. Solution: Strictly control the heating temperature (not exceeding 170℃); shorten the material residence time in the extruder (screw speed 30-50rpm). |
| Systèmes de refroidissement | Water cooling (mold cooling: water temperature 15-25℃); refroidissement de l'air (prototype post-cooling: vitesse de vent de 1 à 2 m / s) | Problème: PS prototype deformation after demolding. Solution: Extend the mold cooling time (8-12 seconds for small prototypes, 15-20 seconds for large ones); after demolding, Placer le prototype sur une grille de refroidissement pour 10-15 minutes (room temperature 20-25℃) to stabilize dimensions. |
| Material Flow Control | Use a screw with a shallow groove (depth 3-5mm) for extrusion; ajouter 0.5-1% lubrifiant (Par exemple, stearic acid) to PS raw materials | Problème: Poor PS material flow, uneven parison. Solution: The shallow-groove screw enhances shearing and mixing of PS; lubricants improve flowability without affecting transparency. |
| Sélection d'outils | Extrusion blow molding: die head with smooth inner wall (RA 0,4 μm); moulage par coup d'injection: preform mold with chrome plating (Améliore la résistance à l'usure) | Problème: PS parison has scratches or uneven thickness. Solution: Regularly polish the die head inner wall to remove impurities; check the preform mold for wear and replace it in time (chrome-plated molds have a service life 2-3 times longer than ordinary steel molds). |
| Optimisation du processus | Adopter “basse température, slow speed” for extrusion blow molding (temperature 150-170℃, speed 8-12mm/s); pour le moulage par coup d'injection, optimize preform cooling time (5-8 secondes) | Problème: High defect rate of PS prototypes (craquage, jaunissant). Solution: Low temperature and slow speed reduce PS thermal decomposition and parison sagging; reasonable preform cooling time ensures the preform maintains its shape during transfer to the blow mold. |
5. Yigu Technology’s Perspective on PS Blow Molding Prototype Processing
À la technologie Yigu, Nous nous concentrons sur “material-technology-design integration” for PS blow molding prototypes. We select high-transparency GPPS (General Purpose Polystyrene) for most prototypes, ajout 3-5% rubber modifiers for brittle-sensitive scenarios. Pour la moulure de soufflage, we prefer injection blow molding for small, pièces de haute précision (tolerances ±0.05mm) and optimize heating with infrared temperature control (accuracy ±2℃). En conception, we use CAD modeling with DFM to avoid sharp corners (R≥3mm) and control wall thickness variation ≤5%. Le contrôle de la qualité comprend 100% inspection visuelle (transparence, fissure) et 15% sampling for impact strength tests. The core is leveraging PS’s advantages while mitigating its brittleness and thermal stability issues to deliver cost-effective, prototypes de haute qualité.
FAQ
1. Why does my PS blow molding prototype turn yellow during processing?
Yellowing is mainly caused by excessive heating temperature or prolonged material residence time. D'abord, check the extruder/mold temperature—reduce the die head temperature by 5-10℃ (to 160-165℃) and the melting zone temperature by 10-15℃ (to 145-155℃). Deuxième, increase the screw speed by 5-10rpm (to 35-40rpm) to shorten the material residence time in the extruder. If yellowing persists, replace the PS raw material (it may have been stored for too long and degraded).
2. How to improve the impact resistance of PS blow molding prototypes without significantly reducing transparency?
The best way is to use impact-modified PS (LES HANCHES, Polystyrène à fort impact) instead of ordinary GPPS. HIPS adds rubber particles during production, which can increase impact strength to 5-10 KJ / (3-5 times that of GPPS) Tout en maintenant 80-90% of GPPS’s transparency. If you must use GPPS, ajouter 3-5% transparent rubber modifiers (Par exemple, methyl methacrylate-butadiene-styrene copolymer, MBS), which can increase impact strength by 2-3 times with only a 5-10% reduction in transparency.
3. What is the best way to solve the problem of PS blow molding prototype sticking to the mold?
D'abord, optimize the mold design: increase the draft angle to 2.5-3° (larger than the usual 2°) and polish the mold cavity surface to Ra 0.4μm (higher than the usual 0.8μm). Deuxième, use a mold release agent suitable for PS—choose water-based mold release agents (avoid oil-based ones, which affect PS’s transparency) and spray a thin layer (0.01-0.02MM) on the mold cavity before each molding cycle. Troisième, extend the mold cooling time by 2-3 secondes (à 10-13 seconds for small prototypes) to make the PS prototype harder when demolding and less likely to stick to the mold.